4 EIS at carbon fiber cylindrical microelectrodes Results and discussion Figure 4.1 shows impedance spectra at two selected potentials. Figure 4.1: Impedance spectra for a carbon fiber. Red points are experimental data at the reversible potential, blue points are at an overpotential of +0.1 V. Black solid lines are fitted curves; dashed lines are extensions into the lower frequency region that was not used in the fit. As usual, the high-frequency semicircle in the Nyquist plots arises from the charge-transfer resistance and double-layer capacitance. The lower frequency feature is the mass transport impedance, which rises to a plateau as predicted. In the case of the reversible potential, at the lowest measured frequencies the imaginary part of the impedance decreased again, possibly due to convection. At higher overpotentials, the low-frequency region became noisy and this decrease was not seen. The value of d determines the frequency at which the rise to the plateau occurs and the value of determines the height of the plateau. 46PDF Image | Electron Transfer Kinetics in Redox Flow Batteries
PDF Search Title:
Electron Transfer Kinetics in Redox Flow BatteriesOriginal File Name Searched:
electron-transfer-flow-batteries-thesis.pdfDIY PDF Search: Google It | Yahoo | Bing
Salgenx Redox Flow Battery Technology: Salt water flow battery technology with low cost and great energy density that can be used for power storage and thermal storage. Let us de-risk your production using our license. Our aqueous flow battery is less cost than Tesla Megapack and available faster. Redox flow battery. No membrane needed like with Vanadium, or Bromine. Salgenx flow battery
CONTACT TEL: 608-238-6001 Email: greg@salgenx.com (Standard Web Page)